Grinding Stones - Grind or Polish Concrete
|
|
|
|
Grinding Stones
|
|
The C06 and C10 is a coarse grade and one of the most popular and provided the maximum material removal rates. They are utilized for general grinding and the
removal of trowel marks., hight spots and rought sections on concrete surfaces. The average servise life is approximately : 4 to 10 hours
The C24 is a medium grade stone that will result in a lower material removal rates. It is utilized for finer finish grinding of concrete and rought grinding
on terrazzo and other tyes of stone floor configurations. The average service life is approximately: 6 to 10 hours.
The C80 is a fine grade stone the will result in still lower material removal rates. It is utilized for polishing concrete and medium grinding on
terrazzo and other tyes of stone floor configurations with a water/slurry mixture only. The average service life is approximately: 8 to 20 hours.
The C120 is a super fine grade stone the will result in still lower material removal rates. It is utilized for final polishing concrete and medium
grinding on terrazzo and other tyes of stone floor configurations with a water/slurry mixture only. The average service life is approximately: 40 to 75 hours.
|
|
Specifications:
|
|
|
|
|
Silicon carbide as the abrasive medium and a clay binder as the matrix.
|
|
|
Remove up to 1/8 inch material thickness. The larger the number, the finer the grain structure and usually, the smoother the resulting finish
|
|
|
Coarse to supper fine grades available
|
|
Hints:
|
C10 stone most popular. Water and slurry minimizes clogging. Do not use to remove any thickness of paints, adhesives, epoxies, etc because of clogging
characteristics similar to sandpaper.
|
|
|
Up to 5000 square feet.
|
|
|
2 inch x 2 inch x 4 inch.
|
Click Here for Application
Chart
|
Diamond (DIAM-A-TACH) - Grind or Polish Concrete
|
|
|
|
Diamonds - DIAM-A-TACH
|
|
White identification color, softer matrix composition, for many general purpose applications. 30 to 40 grit.
Silver identification color, medium matrix composition, for use on epoxy mortar (abrasive) or more abrasive materials. 40 to 50 grit.
Red identification color, finish matrix composition, for use on finish grinding (polishing) applications requiring minimal swirl marks. 100 to 120
grit.
|
|
Specifications:
|
|
|
|
|
Industry stantard diamds
|
|
|
Removal of thin layers of materials without clogging,
including adhesives, epoxies, urethanes, paints and concrete.
|
|
Hints:
|
Segments are directionally marked to increase diamond tail
service life. Normal segment wear: .015 inch per 8 hour day. Variety
of matrix/diamond configurations available. Use wet or dry.
|
|
|
Sanded finsish to a polished finished
|
|
|
Up to 50,000 square feet. (up to 15 time longer than carbide grinding stones)
|
|
|
2 inch x 2 inch x 4 inch.
|
|
DIAM-A-TACH - Grind or Polish Concrete | Segment System
|
|
|
|
Diamonds - DIAM-A-TACH
|
|
The SG24-2300 DIAM-A-TACH Diamond Segment Grinding System offers an innovative solution for a wide variety of surface preparation job applications. The
Omnitrixâ⢠formulation allows the same matrix to be used on green concrete, high tensile epoxies, thin-film type floor coverings and fully cured concrete. Delivers balanced material
removal rates and service life. This unique feature simplifies the proper matrix selection process and minimizes inventory stocking levels.
The rectangular-shaped, diamond segments have significantly greater thickness when compared to competitive products. Delivers substantially longer service
life and higher ROI. The housing is directional marked for proper orientation to eliminate the top layer of tails from being inadvertently removed. Secures tight with a plastic
wedge.
Use the SG24-2300 DIAM-A-TACH Grinding System with General SG12 and SG24 Series Surface Grinders and popular models of competitive single and dual head
surface grinders.
|
|
Specifications:
|
|
|
|
|
Industry stantard diamds
|
|
|
Removal of thin layers of materials without clogging,
including adhesives, epoxies, urethanes, paints and concrete.
|
|
Hints:
|
Unit are directionally marked to increase diamond tail
service life. Normal segment wear: .015 inch per 8 hour day. Single matric formulation for simplicity. Greater diamon segment thickness. Low acquisition cost. Use wet or dry.
|
|
|
Sanded finsish to a polished finished
|
|
|
Up to 50,000 square feet. (up to 15 time longer than carbide grinding stones)
|
|
|
5-5/8ââ¬Ãù (143 mm) L x 2-1/4ââ¬Ãù (57 mm) W x 2-1/4ââ¬Ãù (57 mm) H
|
|
Number of Segments per Unit:
|
4
|
|
Segment Grit:
|
30/40
|
|
Nominal Segment dimensions:
|
2 inch (52 mm) L x .400 inch (10 mm) W x .450 inch (11 mm) H
|
|
Grinding Area per Unit:
|
3.2 inò (520 mmò)
|
|
Weight, each:
|
2-1/4 lbs (1 kg)
|
Click Here for Application
Chart
|
Scarifiers - Grind or Polish Concrete
|
|
|
|
Scarifiers
|
|
Available in carbide tipped 5 point flails for and aggressive chipping action. Also, available in multipoint hardened steel flails for a fine finish or for
breaking up hardened deposits of forring matter or concrete floors.
|
|
Specifications:
|
|
|
|
|
Carbided tipped or hardened steel
|
|
|
Roughen on concrete floors or remove hardened deposits on floors
|
|
Hints:
|
Not recommended for soft or "gummy" deposits.
|
|
|
Very rough finish to no effect to concrete cap.
|
|
|
2 inch x 2 inch x 4 inch
|
Click Here for Application
Chart
|
SCRAPE-R-TACH - Strip Coatings From Surfaces
|
SG24-1900
|
|
|
Coatings Removal System (SCRAPE-R-TACH)
|
|
The SCRAPE-R-TACH floor coatings removal system utilizes two Tungsten Carbide inserts providing 16 wear edges. Designed for removing a wide range of
urethanes, rubber membranes, material buildups, paints, masticd, etc. Production rates of up to several hundred square feet per hour the SCRAPE-R-TACH system bring a quick return on
investment.
|
|
Specifications:
|
|
|
|
|
Tungston carbide
|
|
|
Removal of thicker layers of materials, including:
adhesives, epoxies, urethanes and paints.
|
|
Hints:
|
Tungsten carbide inserts feature 8 wear edges. Test procedure: scrape blunt file edge against surface to determine effectiveness. Use water and sand slurry to
increase productivity on extrudable materials. Add weight to grinder to increase productivity.
|
|
|
Variable from 1 to 8 hours per wear edge.
|
|
|
(1) Quad-SertÃÆâÃÆââ¬Å¡ÃÆââ¬ËÃââ insert: 1 inch x 1 inch
|
Click Here for Application
Chart
|
WIRE BRUSH - Strip Coatings From Surfaces
|
|
|
|
Wire Brush
|
|
Flat steel wires are set in plastic blocks. Brushes quickly remove materials such a softer grease, wax, food by-products and rubber backing during carpet
removal. When producing exposed aggregate slabs, wire brushes clean away the slower setting concrete while not disturbing the aggregate. Other practical uses include roughing linoleum tiles
for the application of urethane coverings, the removal of blistering and peeling paint, plaster droppings and material accumulations from warehouse floors. For increase service life, bushes
should be rotated between discs every hour of operation to remove any directional set. Additional weight added to the grinder will not normally increase productivity rates.
|
|
Specifications:
|
|
|
|
|
Nylon plastic body with flat wire spring steel wire bristles
|
|
|
Remove soft deposit on floor or to "rough" up linoleum floors prior to new covering
|
|
|
2 inch x 2 inch x 4 inch
|